From Wikipedia, the free encyclopedia
(Redirected from Seger cone)
Four Seger cones after use

Pyrometric cones are pyrometric devices that are used to gauge heatwork during the firing of ceramic materials in a kiln. The cones, often used in sets of three, are positioned in a kiln with the wares to be fired and, because the individual cones in a set soften and fall over at different temperatures, they provide a visual indication of when the wares have reached a required state of maturity, a combination of time and temperature.

Pyrometric cones give a temperature equivalent; they are not simple temperature-measuring devices.

Definition

[edit]

The pyrometric cone is "A pyramid with a triangular base and of a defined shape and size; the "cone" is shaped from a carefully proportioned and uniformly mixed batch of ceramic materials so that when it is heated under stated conditions, it will bend due to softening, the tip of the cone becoming level with the base at a definitive temperature. Pyrometric cones are made in series, the temperature interval between the successive cones usually being 20 degrees Celsius. The best known series are Seger Cones (Germany), Orton Cones (USA) and Staffordshire Cones (UK)."[1][2]

Usage

[edit]

For some products, such as porcelain and lead-free glazes, it can be advantageous to fire within a two-cone range. The three-cone system can be used to determine temperature uniformity and to check the performance of an electronic controller. The three-cone system consists of three consecutively numbered cones:

  • Guide cone – one cone number cooler than firing cone.
  • Firing cone – the cone recommended by manufacturer of glaze, slip, etc.
  • Guard cone – one cone number hotter than firing cone.

Additionally, most kilns have temperature differences from top to bottom. The amount of difference depends on the design of the kiln, the age of the heating elements, the load distribution in the kiln, and the cone number to which the kiln is fired. Usually, kilns have a greater temperature difference at cooler cone numbers. Cones should be used on the lower, middle and top shelves to determine how much difference exists during firing. This will aid in the way the kiln is loaded and fired to reduce the difference. Downdraft venting will also even out temperatures variance.

Both temperature and time and sometimes atmosphere affect the final bending position of a cone. Temperature is the predominant variable. The temperature is referred to as an equivalent temperature, since actual firing conditions may vary somewhat from those in which the cones were originally standardized. Observation of cone bending is used to determine when a kiln has reached a desired state. Additionally, small cones or bars can be arranged to mechanically trigger kiln controls when the temperature rises enough for them to deform. Precise, consistent placement of large and small cones must be followed to ensure the proper temperature equivalent is being reached. Every effort needs to be made to always have the cone inclined at 8° from the vertical. Large cones must be mounted 2 inches above the plaque and small cones mounted 15/16 inches. With the cones having their own base, "self-supporting cones" eliminate errors with their mounting.

Pyrometric cones can be used in a "kiln sitter", a device which senses the softening of a cone and produces a mechanical output through a trigger assembly, typically to switch off the kiln.[3]

Control of variability

[edit]

Pyrometric cones are sensitive measuring devices and it is important to users that they should remain consistent in the way that they react to heating. Cone manufacturers follow procedures to control variability (within batches and between batches) to ensure that cones of a given grade remain consistent in their properties over long periods. A number of national standards[4][5][6] and an ISO standard [7] have been published regarding pyrometric cones.

Even though cones from different manufacturers can have relatively similar numbering systems, they are not identical in their characteristics. If a change is made from one manufacturer to another, then allowances for the differences can sometimes be necessary.

History

[edit]

In 1782, Josiah Wedgwood created accurately scaled pyrometric device, with details published in the Philosophical Transactions of the Royal Society of London in 1782 (Vol. LXXII, part 2). This led him to be elected a fellow of the Royal Society.[8][9][10][11] [12]

The modern form of the pyrometric cone was developed by Hermann Seger and first used to control the firing of porcelain wares at the Royal Porcelain Factory, Berlin (Königliche Porzellanmanufaktur, in 1886, where Seger was director.[13] Seger cones are made by a small number of companies and the term is often used as a synonym for pyrometric cones.[14][15] The Standard Pyrometric Cone Company was founded in Columbus, Ohio, by Edward J. Orton, Jr. in 1896 to manufacture pyrometric cones, and following his death a charitable trust established to operate the company, which is known Edward Orton Jr. Ceramic Foundation, or Orton Ceramic Foundation.[16]

Pyrometric cones are often referred to as Orton Cones within the United States, but in his lifetime Orton preferred calling them Seger cones.[17]

I hope no one will ever apply my name to the cone system in any way, because Dr. Seger deserves all the glory which there is in having brought us this most convenient system. My cones are labeled Standard pyrometric cones. I have hesitated to print the term Seger cones on my output because the German cone makers...might feel I was attempting to cut under or defraud them...The name Seger cone will then become a sort of monument to that prominent man, who must always be recognized as the first scientific ceramist of all history.

— Edward Orton Jr., "Remarks on Seger Cones", Clay Record (November 15, 1900)

Ceramic art

[edit]

A biennial ceramic art exhibition for small work, the Orton Cone Box Show,[18] took the Orton Cone company's pyrometric cone box as the size constraint for submissions.

Temperature ranges

[edit]

The following temperature equivalents for pyrometric cones were retrieved from references in the External Links section.

Orton[19] Börkey Keratech[20] Nimra Glass[21] Min Max
Self-Supporting Cones Large Cones Small
Regular — SSB Iron Free — SSK Regular — LRB Iron Free — IFB Regular
Heating Rate: 15°C/hr 60°C/hr 150°C/hr 15°C/hr 60°C/hr 150°C/hr 60°C/hr 150°C/hr 60°C/hr 150°C/hr 300°C/hr 150°C/hr 150°C/hr 20°C/hr 20°C/hr
Type: Slow Medium Fast Slow Medium Fast Medium Fast Medium Fast Fast Normal Laboratory Normal Laboratory
Cone #
022 586°C 590°C 630°C 595°C 605°C 580°C 585°C 590°C 580°C 630°C
021 600°C 617°C 643°C 640°C 650°C 620°C 625°C 610°C 600°C 650°C
020 626°C 638°C 666°C 660°C 675°C 635°C 640°C 635°C 626°C 675°C
019 656°C 678°C 695°C 676°C 693°C 723°C 685°C 695°C 655°C 665°C 685°C 655°C 723°C
018 686°C 715°C 734°C 712°C 732°C 752°C 705°C 715°C 675°C 680°C 725°C 675°C 752°C
017 705°C 738°C 763°C 736°C 761°C 784°C 730°C 735°C 695°C 695°C 750°C 695°C 784°C
016 742°C 772°C 796°C 769°C 794°C 825°C 755°C 760°C 720°C 720°C 786°C 720°C 825°C
015a 780°C 785°C 740°C 750°C 740°C 785°C
015 750°C 791°C 818°C 788°C 816°C 843°C 810°C 750°C 843°C
014a 805°C 815°C 780°C 790°C 780°C 815°C
014 757°C 807°C 838°C 807°C 836°C 870°C 830°C 757°C 870°C
013a 835°C 845°C 840°C 860°C 835°C 860°C
013 807°C 837°C 861°C 837°C 859°C 880°C 860°C 807°C 880°C
012a 860°C 890°C 860°C 880°C 860°C 890°C
012 843°C 861°C 882°C 858°C 880°C 900°C 865°C 843°C 900°C
011a 900°C 900°C 880°C 890°C 880°C 900°C
011 857°C 875°C 894°C 873°C 892°C 915°C 885°C 857°C 915°C
010a 920°C 925°C 900°C 910°C 900°C 925°C
010 891°C 903°C 915°C 871°C 886°C 893°C 898°C 913°C 884°C 891°C 919°C 895°C 871°C 919°C
09a 935°C 940°C 920°C 930°C 920°C 940°C
09 907°C 920°C 930°C 899°C 919°C 928°C 917°C 928°C 917°C 926°C 955°C 925°C 899°C 955°C
08a 955°C 965°C 930°C 940°C 930°C 965°C
08 922°C 942°C 956°C 924°C 946°C 957°C 942°C 954°C 945°C 955°C 983°C 955°C 922°C 983°C
07a 970°C 975°C 950°C 955°C 950°C 975°C
07 962°C 976°C 987°C 953°C 971°C 982°C 973°C 985°C 970°C 980°C 1008°C 980°C 953°C 1008°C
06a 990°C 995°C 970°C 980°C 970°C 995°C
06 981°C 998°C 1013°C 969°C 991°C 998°C 995°C 1011°C 991°C 996°C 1023°C 1000°C 969°C 1023°C
05½ 1004°C 1015°C 1025°C 990°C 1012°C 1021°C 1012°C 1023°C 1011°C 1020°C 1043°C 990°C 1043°C
05a 1000°C 1010°C 990°C 1010°C 990°C 1010°C
05 1021°C 1031°C 1044°C 1013°C 1037°C 1046°C 1030°C 1046°C 1032°C 1044°C 1062°C 1045°C 1013°C 1062°C
04a 1025°C 1055°C 1015°C 1035°C 1015°C 1055°C
04 1046°C 1063°C 1077°C 1043°C 1061°C 1069°C 1060°C 1070°C 1060°C 1067°C 1098°C 1060°C 1043°C 1098°C
03a 1055°C 1070°C 1040°C 1055°C 1040°C 1070°C
03 1071°C 1086°C 1104°C 1066°C 1088°C 1093°C 1086°C 1101°C 1087°C 1091°C 1131°C 1100°C 1066°C 1131°C
02a 1085°C 1100°C 1070°C 1090°C 1070°C 1100°C
02 1078°C 1102°C 1122°C 1084°C 1105°C 1115°C 1101°C 1120°C 1102°C 1113°C 1148°C 1120°C 1078°C 1148°C
01a 1105°C 1125°C 1090°C 1105°C 1090°C 1125°C
01 1093°C 1119°C 1138°C 1101°C 1123°C 1134°C 1117°C 1137°C 1122°C 1132°C 1178°C 1138°C 1093°C 1178°C
1 1109°C 1137°C 1154°C 1119°C 1139°C 1148°C 1136°C 1154°C 1137°C 1146°C 1184°C 1155°C 1109°C 1184°C
1a 1125°C 1145°C 1105°C 1120°C 1105°C 1145°C
2 1112°C 1142°C 1164°C 1142°C 1162°C 1190°C 1160°C 1112°C 1190°C
2a 1150°C 1165°C 1125°C 1135°C 1125°C 1165°C
3 1115°C 1152°C 1170°C 1130°C 1154°C 1162°C 1152°C 1168°C 1151°C 1160°C 1196°C 1170°C 1115°C 1196°C
3a 1170°C 1185°C 1140°C 1150°C 1140°C 1185°C
4 1141°C 1162°C 1183°C 1160°C 1181°C 1209°C 1185°C 1141°C 1209°C
4a 1195°C 1220°C 1160°C 1170°C 1160°C 1220°C
5 1159°C 1186°C 1207°C 1184°C 1205°C 1221°C 1200°C 1159°C 1221°C
1167°C 1203°C 1225°C 1167°C 1225°C
5a 1215°C 1230°C 1175°C 1185°C 1175°C 1230°C
6 1185°C 1222°C 1243°C 1220°C 1241°C 1255°C 1225°C 1185°C 1255°C
6a 1240°C 1260°C 1195°C 1210°C 1195°C 1260°C
7 1201°C 1239°C 1257°C 1237°C 1255°C 1264°C 1260°C 1270°C 1215°C 1230°C 1240°C 1201°C 1270°C
8 1211°C 1249°C 1271°C 1247°C 1269°C 1300°C 1280°C 1295°C 1240°C 1255°C 1260°C 1211°C 1300°C
9 1224°C 1260°C 1280°C 1257°C 1278°C 1317°C 1300°C 1315°C 1255°C 1270°C 1280°C 1224°C 1317°C
10 1251°C 1285°C 1305°C 1282°C 1303°C 1330°C 1320°C 1330°C 1280°C 1290°C 1300°C 1251°C 1330°C
11 1272°C 1294°C 1315°C 1293°C 1312°C 1336°C 1340°C 1350°C 1300°C 1315°C 1315°C 1272°C 1350°C
12 1285°C 1306°C 1326°C 1304°C 1324°C 1355°C 1360°C 1375°C 1330°C 1340°C 1330°C 1285°C 1375°C
13 1310°C 1331°C 1348°C 1321°C 1346°C 1380°C 1395°C 1360°C 1375°C 1345°C 1310°C 1395°C
14 1351°C 1365°C 1384°C 1388°C 1366°C 1400°C 1410°C 1370°C 1395°C 1365°C 1351°C 1410°C
15 1425°C 1440°C 1400°C 1420°C 1430°C 1400°C 1440°C
16 1445°C 1470°C 1425°C 1445°C 1475°C 1425°C 1475°C
17 1480°C 1500°C 1445°C 1465°C 1485°C 1445°C 1500°C
18 1500°C 1520°C 1470°C 1480°C 1505°C 1470°C 1520°C
19 1515°C 1540°C 1495°C 1505°C 1530°C 1495°C 1540°C
20 1530°C 1560°C 1515°C 1530°C 1550°C 1515°C 1560°C
21 1570°C 1570°C 1570°C
23 1540°C --- --- --- 1591°C 1540°C 1591°C
26 1560°C 1580°C --- --- 1607°C 1560°C 1607°C
27 1595°C 1600°C --- --- 1595°C 1600°C
27½ --- 1620°C --- --- 1620°C 1620°C
28 1605°C 1640°C --- --- 1605°C 1640°C
29 1635°C 1660°C --- --- 1635°C 1660°C
30 1655°C 1680°C --- --- 1655°C 1680°C
31 1680°C 1700°C --- --- 1680°C 1700°C
32 1695°C 1710°C --- --- 1695°C 1710°C
32½ --- 1720°C --- --- 1720°C 1720°C
33 1710°C 1730°C --- --- 1710°C 1730°C
33½ --- 1740°C --- --- 1740°C 1740°C
34 1725°C 1760°C --- --- 1725°C 1760°C
35 1765°C 1780°C --- --- 1765°C 1780°C
36 1790°C 1800°C --- --- 1790°C 1800°C
37 1815°C 1830°C --- --- 1815°C 1830°C
38 1840°C 1860°C --- --- 1840°C 1860°C
39 1860°C 1880°C --- --- 1860°C 1880°C
40 1880°C 1900°C --- --- 1880°C 1900°C
41 1915°C 1940°C --- --- 1915°C 1940°C
42 1955°C 1980°C --- --- 1955°C 1980°C

Notes

[edit]
  1. ^ Dodd and Murfin, A. and D. (1994). Dictionary Of Ceramics. 3rd edition. Cambridge: Institute of Materials. Woodhead Publishing Limited. ISBN 0-901716-56-1.
  2. ^ Edward Orton Jr. Ceramic Foundation
  3. ^ "The Definitive Guide to Kiln Controllers : Manual vs Automatic". Soul Ceramics. Archived from the original on 2023-12-09. Retrieved 2024-07-06.
  4. ^ "Japan Pyrometric reference cones".
  5. ^ "China's Refractories".
  6. ^ "ASTM C24 Standard Test Method for Pyrometric Cone Equivalency(PCE) of Fireclay and High Alumina Refractory Materials".
  7. ^ "ISO 1146:1988-02".
  8. ^ "Wedgwood Pyrometer by J. Newman, 1827-56 | Science Museum Group Collection".
  9. ^ "Museo Galileo - Wedgwood pyrometer".
  10. ^ "Image of wedgwood pyrometer, 1786. By Science & Society Picture Library".
  11. ^ Sella, Andrea (18 December 2012). "Wedgwood's pyrometer". Chemistry World.
  12. ^ "Philosophical Transactions of the Royal Society of London. Vol. LXXII. For the Year 1782. Part II". The London Medical Journal. 4 (3): 225–235. 1783. PMC 5545481.
  13. ^ Lange, P. (1991). "Role of August Hermann Seger in the development of silicate technology". Ceram. Forum Int./Ber. DKG. 68 (1/2).
  14. ^ "The Seger Cone: 100 years old". Osterr. Keram. Rundsch. 23 (9/10): 9.
  15. ^ Joger, A. (1985). "100 years 'Seger Cone'". Silikattechnik. 36 (12): 400.
  16. ^ "Orton Company History".
  17. ^ Gorton, Elmer (November 15, 1900). "Remarks on Seger Cones". Clay Record. 17: 15.
  18. ^ "Cone Box Show".
  19. ^ "Temperature Equivalents for Orton Pyrometric Cones (°C)" (PDF). Edward Orton Jr. Ceramic Foundation. Retrieved 17 January 2020.
  20. ^ "Temperature equivalents table of Seger pyrometric cones". Börkey Keratech. Archived from the original on 2011-07-18. Retrieved 17 January 2020.
  21. ^ "Nimra Glass Temperature Conversion Chart". Nimra Cerglass Technics (P) Ltd. Retrieved 17 January 2020.

References

[edit]