From Wikipedia, the free encyclopedia
(Redirected from Heusler alloys)
In the case of the full Heusler compounds with formula X2YZ (e.g., Co2MnSi) two of them are occupied by X atoms (L21 structure); for the half-Heusler compounds XYZ one fcc sublattice remains unoccupied (C1b structure).

Heusler compounds are magnetic intermetallics with face-centered cubic crystal structure and a composition of XYZ (half-Heuslers) or X2YZ (full-Heuslers), where X and Y are transition metals and Z is in the p-block. The term derives from the name of German mining engineer and chemist Friedrich Heusler, who studied such a compound (Cu2MnAl) in 1903.[1] Many of these compounds exhibit properties relevant to spintronics, such as magnetoresistance, variations of the Hall effect, ferro-, antiferro-, and ferrimagnetism, half- and semimetallicity, semiconductivity with spin filter ability, superconductivity, topological band structure and are actively studied as thermoelectric materials. Their magnetism results from a double-exchange mechanism between neighboring magnetic ions. Manganese, which sits at the body centers of the cubic structure, was the magnetic ion in the first Heusler compound discovered. (See the Bethe–Slater curve for details of why this happens.)

Styles of writing chemical formula

[edit]

Depending on the field of literature being surveyed, one might encounter the same compound referred to with different chemical formulas. An example of the most common difference is X2YZ versus XY2Z, where the labels of the two transition metals X and Y in the compound are swapped. The traditional convention X2YZ [2] arises from the interpretation of Heuslers as intermetallics and is used predominantly in literature studying magnetic applications of Heuslers compounds. The XY2Z convention on the other hand is used mostly in thermoelectric materials[3] and transparent conducting applications [4] literature where semiconducting Heuslers (most half-Heuslers are semiconductors) are used. This convention, in which the left-most element on the periodic table comes first, uses the Zintl interpretation[5] of semiconducting compounds where the chemical formula XY2Z is written in order of increasing electronegativity. In well-known compounds such as Fe2VAl which were historically thought of as metallic (semi-metallic) but were more recently shown to be small-gap semiconductors[6] one might find both styles being used. In the present article semiconducting compounds might sometimes be mentioned in the XY2Z style.

"Off-stoichiometric" Heuslers

[edit]
Phase diagrams sketches demonstrating how Double and Triple Half-Heusler compositions are different from traditional alloy compositions. [7]

Although traditionally thought to form at compositions XYZ and X2YZ, studies published after 2015 have discovered and reliably predicted Heusler compounds with atypical compositions such as XY0.8Z and X1.5YZ.[8][9] Besides these ternary compositions, quaternary Heusler compositions called the double Half-Heusler X2YY'Z2 [10] (e.g. Ti2FeNiSb2) and triple Half-Heusler X2X'Y3Z3 [7] (for e.g. Mg2VNi3Sb3) have also been discovered. These "off-stoichiometric" (that is, differing from the well-known XYZ and X2YZ compositions) Heuslers are mostly semiconductors in the low temperature T = 0 K limit.[11] The stable compositions and corresponding electrical properties for these compounds can be quite sensitive to temperature[12] and their order-disorder transition temperatures often occur below room-temperatures.[10] Large amounts of defects at the atomic scale in off-stoichiometric Heuslers helps them achieve very low thermal conductivities and make them favorable for thermoelectric applications.[13][14] The X1.5YZ semiconducting composition is stabilized by the transition metal X playing a dual role (electron donor as well as acceptor) in the structure.[15]

Half-Heusler thermoelectrics

[edit]
A schematic of a HH thermoelectric. X and Z have a larger electronegativity difference between them and form an NaCl-type ionic sublattice while Y and Z form a ZnS-type covalent sublattice

The half-Heusler compounds have distinctive properties and high tunability which makes the class very promising as thermoelectric materials. A study has predicted that there can be as many as 481 stable half-Heusler compounds using high-throughput ab initio calculation combine with machine learning techniques.[16] The particular half-Heusler compounds of interest as thermoelectric materials (space group ) are the semiconducting ternary compounds with a general formula XYZ where X is a more electropositive transition metal (such as Ti or Zr), Y is a less electropositive transition metal (such Ni or Co), and Z is heavy main group element (such as Sn or Sb).[17][18] This flexible range of element selection allows many different combinations to form a half-Heusler phase and enables a diverse range of material properties.

Half-Heusler thermoelectric materials have distinct advantages over many other thermoelectric materials; low toxicity, inexpensive element, robust mechanical properties, and high thermal stability make half-Heusler thermoelectrics an excellent option for mid-high temperature application.[17][19] However, the high thermal conductivity, which is intrinsic to highly symmetric HH structure, has made HH thermoelectric generally less efficient than other classes of TE materials. Many studies have focused on improving HH thermoelectric by reducing the lattice thermal conductivity and zT > 1 has been repeatedly recorded.[19]

List of common half-Heusler compounds[20]
p-type n-type
MFeSb (M = V, Nb, Ta) MCoSb (M = Ti, Zr, Hf)
ZrCoBi MNiSn (M = Ti, Zr, Hf)
MCoSb (M = Ti, Zr, Hf) M0.8CoSb (M = V, Nb, Ta)

Magnetic properties

[edit]

The magnetism of the early full-Heusler compound Cu2MnAl varies considerably with heat treatment and composition.[21] It has a room-temperature saturation induction of around 8,000 gauss, which exceeds that of the element nickel (around 6100 gauss) but is smaller than that of iron (around 21500 gauss). For early studies see.[1][22][23] In 1934, Bradley and Rogers showed that the room-temperature ferromagnetic phase was a fully ordered structure of the L21 Strukturbericht type.[24] This has a primitive cubic lattice of copper atoms with alternate cells body-centered by manganese and aluminium. The lattice parameter is 5.95 Å. The molten alloy has a solidus temperature of about 910 °C. As it is cooled below this temperature, it transforms into disordered, solid, body-centered cubic beta-phase. Below 750 °C, a B2 ordered lattice forms with a primitive cubic copper lattice, which is body-centered by a disordered manganese-aluminium sublattice.[21][25] Cooling below 610 °C causes further ordering of the manganese and aluminium sub-lattice to the L21 form.[21][26] In non-stoichiometric alloys, the temperatures of ordering decrease, and the range of anealing temperatures, where the alloy does not form microprecipitates, becomes smaller than for the stoichiometric material.[27][28][21]

Oxley found a value of 357 °C for the Curie temperature, below which the compound becomes ferromagnetic.[29] Neutron diffraction and other techniques have shown that a magnetic moment of around 3.7 Bohr magnetons resides almost solely on the manganese atoms.[21][30] As these atoms are 4.2 Å apart, the exchange interaction, which aligns the spins, is likely indirect and is mediated through conduction electrons or the aluminium and copper atoms.[29][31]

Electron microscope images of Cu-Mn-Al Heusler compound showing magnetic domain walls tied to APB's (a) L21 antiphase boundaries by <111> dark-field imaging - the remaining micrographs are in bright-field so that the APB's are not in contrast (b) magnetic domains by Foucault (displaced aperture) imaging, and (c) magnetic domain walls by Fresnel (defocus) imaging.

Electron microscopy studies demonstrated that thermal antiphase boundaries (APBs) form during cooling through the ordering temperatures, as ordered domains nucleate at different centers within the crystal lattice and are often out of step with each other where they meet.[21][25] The anti-phase domains grow as the alloy is annealed. There are two types of APBs corresponding to the B2 and L21 types of ordering. APBs also form between dislocations if the alloy is deformed. At the APB the manganese atoms will be closer than in the bulk of the alloy and, for non-stoichiometric alloys with an excess of copper (e.g. Cu2.2MnAl0.8), an antiferromagnetic layer forms on every thermal APB.[32] These antiferromagnetic layers completely supersede the normal magnetic domain structure and stay with the APBs if they are grown by annealing the alloy. This significantly modifies the magnetic properties of the non-stoichiometric alloy relative to the stoichiometric alloy which has a normal domain structure. Presumably this phenomenon is related to the fact that pure manganese is an antiferromagnet although it is not clear why the effect is not observed in the stoichiometric alloy. Similar effects occur at APBs in the ferromagnetic alloy MnAl at its stoichiometric composition.[citation needed]

Some Heusler compounds also exhibit properties of materials known as ferromagnetic shape-memory alloys. These are generally composed of nickel, manganese and gallium and can change their length by up to 10% in a magnetic field.[33]

Mechanical properties

[edit]

Understanding the mechanical properties of Heusler compounds is paramount for temperature-sensitive applications (e.g. thermoelectrics) for which some sub-classes of Heusler compounds are used. However, experimental studies are rarely encountered in literature.[34] In fact, the commercialization of these compounds is limited by the material's ability to undergo intense, repetitive thermal cycling and resist cracking from vibrations. An appropriate measure for crack resistance is the material's toughness, which typically scales inversely with another important mechanical property: the mechanical strength. In this section, we highlight existing experimental and computational studies on the mechanical properties of Heusler alloys. Note that the mechanical properties of such a compositionally-diverse class of materials is expectedly dependent on the chemical composition of the alloys themselves, and therefore trends in mechanical properties are difficult to identify without a case-by-case study.

The elastic modulus values of half-Heusler alloys range from 83 to 207 GPa, whereas the bulk modulus spans a tighter range from 100 GPa in HfNiSn to 130 GPa in TiCoSb.[34] A collection of various density functional theory (DFT) calculations show that half-Heusler compounds are predicted to have a lower elastic, shear, and bulk modulus than in quaternary-, full-, and inverse-Hausler alloys.[34] DFT also predicts a decrease in elastic modulus with temperature in Ni2XAl (X=Sc, Ti, V), as well as an increase in stiffness with pressure.[35] The decrease in modulus with respect to temperature is also observed in TiNiSn, ZrNiSn, and HfNiSn, where ZrNiSn has the highest modulus and Hf has the lowest.[36] This phenomenon can be explained by the fact that the elastic modulus decreases with increasing interatomic separation: as temperature increases, the atomic vibrations also increase, resulting in a larger equilibrium interatomic separation.

The mechanical strength is also rarely studied in Heusler compounds. One study has shown that, in off-stoichiometric Ni2MnIn, the material reaches a peak strength of 475 MPa at 773 K, which drastically reduces to below 200 MPa at 973 K.[37] In another study, a polycrystalline Heusler alloy composed of the Ni-Mn-Sn ternary composition space was found to possess a peak compressive strength of about 2000 MPa with plastic deformation up to 5%.[38] However, the addition of Indium to the Ni-Mn-Sn ternary alloy not only increases the porosity of the samples, but it also reduces the compressive strength to 500 MPa. It is unclear from the study what percentage of the porosity increase from the indium addition reduces the strength. Note that this is opposite to the outcome expected from solid solution strengthening, where adding indium to the ternary system slows dislocation movement through dislocation-solute interaction and subsequently increases the material's strength.

The fracture toughness can also be tuned with composition modifications. For example, the average toughness of Ti1−x(Zr, Hf)xNiSn ranges from 1.86 MPa m1/2 to 2.16 MPa m1/2, increasing with Zr/Hf content.[36] The preparation of samples may affect the measured fracture toughness however, as elaborated by O’Connor et al.[39] In their study, samples of Ti0.5Hf0.5Co0.5Ir0.5Sb1−xSnx were prepared using three different methods: a high-temperature solid state reaction, high-energy ball milling, and a combination of both. The study found higher fracture toughness in samples prepared without a high-energy ball milling step of 2.7 MPa m1/2 to 4.1 MPa m1/2, as opposed to samples that were prepared with ball milling of 2.2 MPa m1/2 to 3.0 MPa m1/2.[36][39] Fracture toughness is sensitive to inclusions and existing cracks in the material, so it is as expected dependent on the sample preparation.


Half-metallic ferromagnetic Heusler compounds

[edit]

Half-metallic ferromagnets exhibit a metallic behavior in one spin channel and an insulating behavior in the other spin channel. The first example of Heusler half-metallic ferromagnets was first investigated by de Groot et al.,[40] with the case of NiMnSb. Half-metallicity leads to the full polarization of the conducting electrons. Half metallic ferromagnets are therefore promising for spintronics applications.[41]

List of notable Heusler compounds

[edit]
  • Cu2MnAl, Cu2MnIn, Cu2MnSn
  • Ni2MnAl, Ni2MnIn, Ni2MnSn, Ni2MnSb, Ni2MnGa
  • Co2MnAl, Co2MnSi, Co2MnGa, Co2MnGe, Co2NiGa, Co2MnSn
  • Pd2MnAl, Pd2MnIn, Pd2MnSn, Pd2MnSb
  • Co2FeSi, Co2FeAl[42]
  • Fe2VAl
  • Mn2VGa, Co2FeGe[43]
  • Co2CrxFe1−xX(X=Al, Si)[44]
  • YbBiPt[45]

References

[edit]
  1. ^ a b Heusler F. (1903). "Über magnetische Manganlegierungen". Verhandlungen der Deutschen Physikalischen Gesellschaft (in German). 12: 219.
  2. ^ Graf, Tanja; Felser, Claudia; Parkin, Stuart (2011). "Simple rules for the understanding of Heusler compounds". Progress in Solid State Chemistry. 39 (1): 1–50. doi:10.1016/j.progsolidstchem.2011.02.001.
  3. ^ Fu, Chenguang; Bai, Shengqiang; Liu, Yintu; Tang, Yunshan; Chen, Lidong; Zhao, Xinbing; Zhu, Tiejun (2015). "Realizing high figure of merit in heavy-band p-type half-Heusler thermoelectric materials". Nature Communications. 6: 8144. Bibcode:2015NatCo...6.8144F. doi:10.1038/ncomms9144. PMC 4569725. PMID 26330371. S2CID 9626544.
  4. ^ Yan, Feng; Zhang, Xiuwen; Yu, Yonggang; Yu, Liping; Nagaraja, Arpun; Mason, Thomas; Zunger, Alex (2015). "Design and discovery of a novel half-Heusler transparent hole conductor made of all-metallic heavy elements". Nature Communications. 6: 7308. arXiv:1406.0872. Bibcode:2015NatCo...6.7308Y. doi:10.1038/ncomms8308. PMID 26106063. S2CID 5443063.
  5. ^ Zeier, Wolfgang; Schmitt, Jennifer; Hautier, Geoffroy; Aydemir, Umut; Gibbs, Zachary; Felser, Claudia; Snyder, Jeff (2016). "Engineering half-Heusler thermoelectric materials using Zintl chemistry". Nature Reviews Materials. 1 (6): 16032. Bibcode:2016NatRM...116032Z. doi:10.1038/natrevmats.2016.32.
  6. ^ Anand, Shashwat; Gurunathan, Ramya; Soldi, Thomas; Borgsmiller, Leah; Orenstein, Rachel; Snyder, Jeff (2020). "Thermoelectric transport of semiconductor full-Heusler VFe2Al". Journal of Materials Chemistry C. 8 (30): 10174–10184. doi:10.1039/D0TC02659J. S2CID 225448662.
  7. ^ a b Imasato, Kazuki; Sauerschnig, Philipp; Anand, Shashwat; Ishida, Takao; Yamamoto, Atsushi; Ohta, Michihiro (2022). "Discovery of triple half-Heusler Mg2VNi3Sb3 with low thermal conductivity". Journal of Materials Chemistry A. 10 (36): 18737–18744. doi:10.1039/D2TA04593A. S2CID 251456801.
  8. ^ Zeier, Wolfgang; Anand, Shashwat; Huang, Lihong; He, Ran; Zhang, Hao; Ren, Zhifeng; Wolverton, Chris; Snyder, Jeff (2017). "Using the 18-Electron Rule To Understand the Nominal 19-Electron Half-Heusler NbCoSb with Nb Vacancies". Chemistry of Materials. 29 (3): 1210–1217. doi:10.1021/acs.chemmater.6b04583. OSTI 1388395.
  9. ^ Naghibolashrafi, N; Keshavarz, S; Hegde, Vinay; Gupta, A; Butler, W; Romero, J; Munira, K; LeClair, P; Mazumdar, D; Ma, J; Ghosh, A; Wolverton, Chris (2016). "Synthesis and characterization of Fe-Ti-Sb intermetallic compounds: Discovery of a new Slater-Pauling phase". Physical Review B. 93 (104424): 1–11. Bibcode:2016PhRvB..93j4424N. doi:10.1103/PhysRevB.93.104424.
  10. ^ a b Anand, Shashwat; Wood, Max; Xia, Yi; Wolverton, Chris; Snyder, Jeff (2019). "Double Half-Heuslers". Joule. 3 (5): 1226–1238. arXiv:1901.09800. Bibcode:2019Joule...3.1226A. doi:10.1016/j.joule.2019.04.003. S2CID 146680763.
  11. ^ Anand, Shashwat; Xia, Kaiyang; Hegde, Vinay; Aydemir, Umut; Kocevski, Vancho; Zhu, Tiejun; Wolverton, Chris; Snyder, Jeff (2018). "A valence balanced rule for discovery of 18-electron half-Heuslers with defects". Energy and Environmental Science. 11 (6): 1480–1488. doi:10.1039/C8EE00306H. OSTI 1775288.
  12. ^ Anand, Shashwat; Xia, Kaiyang; Zhu, Tiejun; Wolverton, Chris; Snyder, Jeff (2018). "Temperature Dependent n-Type Self Doping in Nominally 19-Electron Half-Heusler Thermoelectric Materials". Advanced Energy Materials. 8 (30): 1–6. Bibcode:2018AdEnM...801409A. doi:10.1002/aenm.201801409. OSTI 1775289. S2CID 104920752.
  13. ^ Xia, Kaiyang; Liu, Yintu; Anand, Shashwat; Snyder, Jeff; Xin, Jiazhan; Yu, Junjie; Zhao, Xinbing; Zhu, Tiejun (2018). "Enhanced Thermoelectric Performance in 18-Electron Nb0.8CoSb Half-Heusler Compound with Intrinsic Nb Vacancies". Advanced Functional Materials. 28 (9). doi:10.1002/adfm.201705845. OSTI 1470455. S2CID 102670058.
  14. ^ Dong, Zirui; Luo, Jun; Wang, Chenyang; Jiang, Ying; Tan, Shihua; Zhang, Yubo; Grin, Yuri; Yu, Zhiyang; Guo, Kai; Zhang, Jiye; Zhang, Wenqing (2022). "Half-Heusler-like compounds with wide continuous compositions and tunable p- to n-type semiconducting thermoelectrics". Nature Communications. 13 (1): 35. Bibcode:2022NatCo..13...35D. doi:10.1038/s41467-021-27795-3. PMC 8748599. PMID 35013264.
  15. ^ Anand, Shashwat; Snyder, Jeff (2022). "Structural Understanding of the Slater–Pauling Electron Count in Defective Heusler Thermoelectric TiFe1.5Sb as a Valence Balanced Semiconductor". ACS Applied Electronic Materials. 4 (7): 3392–3398. doi:10.1021/acsaelm.2c00577. S2CID 250011820.
  16. ^ Legrain, Fleur; Carrete, Jesús; van Roekeghem, Ambroise; Madsen, Georg K.H.; Mingo, Natalio (2018-01-18). "Materials Screening for the Discovery of New Half-Heuslers: Machine Learning versus ab Initio Methods". The Journal of Physical Chemistry B. 122 (2): 625–632. arXiv:1706.00192. doi:10.1021/acs.jpcb.7b05296. ISSN 1520-6106. PMID 28742351. S2CID 19078928.
  17. ^ a b Zeier, Wolfgang G.; Schmitt, Jennifer; Hautier, Geoffroy; Aydemir, Umut; Gibbs, Zachary M.; Felser, Claudia; Snyder, G. Jeffrey (June 2016). "Engineering half-Heusler thermoelectric materials using Zintl chemistry". Nature Reviews Materials. 1 (6): 16032. Bibcode:2016NatRM...116032Z. doi:10.1038/natrevmats.2016.32. ISSN 2058-8437.
  18. ^ Zhu, Tiejun; Fu, Chenguang; Xie, Hanhui; Liu, Yintu; Zhao, Xinbing (October 2015). "High Efficiency Half-Heusler Thermoelectric Materials for Energy Harvesting". Advanced Energy Materials. 5 (19): 1500588. Bibcode:2015AdEnM...500588Z. doi:10.1002/aenm.201500588. S2CID 97616491.
  19. ^ a b Poon, S Joseph (2019-12-04). "Half Heusler compounds: promising materials for mid-to-high temperature thermoelectric conversion". Journal of Physics D: Applied Physics. 52 (49): 493001. arXiv:1905.03845. Bibcode:2019JPhD...52W3001P. doi:10.1088/1361-6463/ab3d71. ISSN 0022-3727. S2CID 150373711.
  20. ^ Quinn, Robert J.; Bos, Jan-Willem G. (2021). "Advances in half-Heusler alloys for thermoelectric power generation". Materials Advances. 2 (19): 6246–6266. doi:10.1039/D1MA00707F. ISSN 2633-5409. S2CID 240534347.
  21. ^ a b c d e f Bouchard M. (1970). "Electron metallography and magnetic properties Cu-Mn-Al heusler alloys". Ph.D. Thesis, Imperial College London.
  22. ^ Knowlton, A. A; Clifford, O. C (1912). "The Heusler alloys". Transactions of the Faraday Society. 8: 195. doi:10.1039/TF9120800195.
  23. ^ Bozorth, Richard M. (1993). Ferromagnetism. Wiley-VCH. p. 201. ISBN 978-0-7803-1032-2.
  24. ^ Bradley, A. J; Rodgers, J. W (1934). "The Crystal Structure of the Heusler Alloys". Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences. 144 (852): 340–59. Bibcode:1934RSPSA.144..340B. doi:10.1098/rspa.1934.0053. S2CID 136873764.
  25. ^ a b Nesterenko, E.G.; Osipenko, I.A.; Firstov, S.A. (1969). "Structure of Cu-Mn-Al Ordered Alloys". Physics of Metals and Metallography. 27 (1): 135–40.
  26. ^ Ohoyama, T; Webster, P J; Tebble, R S (1968). "The ordering temperature of Cu2MnAl". Journal of Physics D: Applied Physics. 1 (7): 951. Bibcode:1968JPhD....1..951O. doi:10.1088/0022-3727/1/7/421. S2CID 250818976.
  27. ^ West D.R.F.; Lloyd Thomas D. (1956). "The constitution of copper rich alloys of the copper-manganese-aluminum system". Journal of Industrial Metals. 85: 97.
  28. ^ Johnston, G.B; Hall, E.O (1968). "Studies on the Heusler alloys—I. Cu2MnAl and associated structures". Journal of Physics and Chemistry of Solids. 29 (2): 193–200. Bibcode:1968JPCS...29..193J. doi:10.1016/0022-3697(68)90062-0.
  29. ^ a b Oxley, D. P; Tebble, R. S; Williams, K. C (1963). "Heusler Alloys". Journal of Applied Physics. 34 (4): 1362. Bibcode:1963JAP....34.1362O. doi:10.1063/1.1729511.
  30. ^ Endō, Keizo; Ohoyama, Tetuo; Kimura, Ren'iti (1964). "On the Magnetic Moment of Mn in Aluminum Heusler Alloy". Journal of the Physical Society of Japan. 19 (8): 1494. Bibcode:1964JPSJ...19.1494E. doi:10.1143/JPSJ.19.1494.
  31. ^ Geldart, D. J. W; Ganguly, P (1970). "Hyperfine Fields and Curie Temperatures of the Heusler Alloys Cu2MnAl, Cu2MnIn, and Cu2MnSn". Physical Review B. 1 (7): 3101–8. Bibcode:1970PhRvB...1.3101G. doi:10.1103/PhysRevB.1.3101.
  32. ^ Lapworth, A. J; Jakubovics, J. P (2006). "Effect of antiphase boundaries on the magnetic properties of Cu-Mn-Al Heusler alloys". Philosophical Magazine. 29 (2): 253. Bibcode:1974PMag...29..253L. doi:10.1080/14786437408213271.
  33. ^ Sakon, Takuo; Otsuka, Kohei; Matsubayashi, Junpei; Watanabe, Yuushi; Nishihara, Hironori; Sasaki, Kenta; Yamashita, Satoshi; Umetsu, Rie; Nojiri, Hiroyuki; Kanomata, Takeshi (2014). "Magnetic Properties of the Ferromagnetic Shape Memory Alloys Ni50+xMn27−xGa23 in Magnetic Fields". Materials. 7 (5): 3715–3734. Bibcode:2014Mate....7.3715S. doi:10.3390/ma7053715. PMC 5453230. PMID 28788645.
  34. ^ a b c Everhart, Wesley; Newkirk, Joseph (2019-05-01). "Mechanical properties of Heusler alloys". Heliyon. 5 (5): e01578. Bibcode:2019Heliy...501578E. doi:10.1016/j.heliyon.2019.e01578. ISSN 2405-8440. PMC 6506478. PMID 31080903.
  35. ^ Wen, Zhiqin; Zhao, Yuhong; Hou, Hua; Wang, Bing; Han, Peide (2017-01-15). "The mechanical and thermodynamic properties of Heusler compounds Ni2XAl (X=Sc, Ti, V) under pressure and temperature: A first-principles study". Materials & Design. 114: 398–403. doi:10.1016/j.matdes.2016.11.005. ISSN 0264-1275.
  36. ^ a b c Rogl, G.; Grytsiv, A.; Gürth, M.; Tavassoli, A.; Ebner, C.; Wünschek, A.; Puchegger, S.; Soprunyuk, V.; Schranz, W.; Bauer, E.; Müller, H. (2016-04-01). "Mechanical properties of half-Heusler alloys". Acta Materialia. 107: 178–195. Bibcode:2016AcMat.107..178R. doi:10.1016/j.actamat.2016.01.031. ISSN 1359-6454.
  37. ^ Musabirov, I. I.; Safarov, I. M.; Nagimov, M. I.; Sharipov, I. Z.; Koledov, V. V.; Mashirov, A. V.; Rudskoi, A. I.; Mulyukov, R. R. (2016-08-01). "Fine-grained structure and properties of a Ni2MnIn alloy after a settling plastic deformation". Physics of the Solid State. 58 (8): 1605–1610. Bibcode:2016PhSS...58.1605M. doi:10.1134/S1063783416080217. ISSN 1090-6460. S2CID 126021631.
  38. ^ Maziarz, W.; Wójcik, A.; Grzegorek, J.; Żywczak, A.; Czaja, P.; Szczerba, M. J.; Dutkiewicz, J.; Cesari, E. (2017-08-25). "Microstructure, magneto-structural transformations and mechanical properties of Ni50Mn37.5Sn12.5-xInx (x=0, 2, 4, 6 % at.) metamagnetic shape memory alloys sintered by vacuum hot pressing". Journal of Alloys and Compounds. 715: 445–453. doi:10.1016/j.jallcom.2017.04.280. ISSN 0925-8388.
  39. ^ a b O'Connor, C.J. (2012). Nanostructured Composite Materials for High Temperature Thermoelectric Energy Conversion, Final Technical Report, DARPA Grant No. HR0011-08-0084 (Report) – via Advanced Materials Research Institute, University of New Orleans.
  40. ^ de Groot, R. A.; Mueller, F. M.; Engen, P. G. van; Buschow, K. H. J. (1983-06-20). "New Class of Materials: Half-Metallic Ferromagnets". Physical Review Letters. 50 (25): 2024–2027. Bibcode:1983PhRvL..50.2024D. doi:10.1103/PhysRevLett.50.2024.
  41. ^ Wollmann, Lukas; Nayak, Ajaya K.; Parkin, Stuart S.P.; Felser, Claudia (2017-07-03). "Heusler 4.0: Tunable Materials". Annual Review of Materials Research. 47 (1): 247–270. arXiv:1612.05947. doi:10.1146/annurev-matsci-070616-123928. ISSN 1531-7331. S2CID 119390317.
  42. ^ Husain, Sajid; Akansel, Serkan; Kumar, Ankit; Svedlindh, Peter; Chaudhary, Sujeet (2016). "Growth of Co2FeAl Heusler alloy thin films on Si(100) having very small Gilbert damping by Ion beam sputtering". Scientific Reports. 6: 28692. Bibcode:2016NatSR...628692H. doi:10.1038/srep28692. PMC 4928049. PMID 27357004.
  43. ^ Ramesh Kumar, K; Kamala Bharathi, K; Arout Chelvane, J; Venkatesh, S; Markandeyulu, G; Harishkumar, N (2009). "First-Principles Calculation and Experimental Investigations on Full-Heusler Alloy Co2FeGe". IEEE Transactions on Magnetics. 45 (10): 3997–9. Bibcode:2009ITM....45.3997K. doi:10.1109/TMAG.2009.2022748. S2CID 33360474.
  44. ^ Guezlane Mourad, H; Baaziz, Z; Charifi, Y; Djaballah (2016). "Electronic, magnetic and thermal properties of Co2CrxFe1−xX(X=Al, Si) Heusler alloys: First-principles calculations". Magnetism and Magnetic Materials. 414: 219–226. Bibcode:2016NatSR...628692H. doi:10.1016/j.jmmm.2016.04.056.
  45. ^ Chadov, Stanislav; Qi, Xiaoliang; Kübler, Jürgen; Fecher, Gerhard H.; Felser, Claudia; Zhang, Shou Cheng (July 2010). "Tunable multifunctional topological insulators in ternary Heusler compounds". Nature Materials. 9 (7): 541–545. arXiv:1003.0193. Bibcode:2010NatMa...9..541C. doi:10.1038/nmat2770. PMID 20512154. S2CID 32178219.

Further reading

[edit]
  • M Guezlane, H Baaziz, F El Haj Hassan, Z Charifi, Y Djaballah, "Electronic, magnetic and thermal properties of Co2CrxFe1− xX (X= Al, Si) Heusler alloys: First-principles calculations", Journal of Magnetism and Magnetic Materials, vol. 414, 2016, p. 219-226 (DOI https://doi.org/10.1016/j.jmmm.2016.04.056,
  • Block, T; Carey, M. J; Gurney, B. A; Jepsen, O (2004). "Band-structure calculations of the half-metallic ferromagnetism and structural stability of full- and half-Heusler phases". Physical Review B. 70 (20): 205114. Bibcode:2004PhRvB..70t5114B. doi:10.1103/PhysRevB.70.205114.
  • Webster, Peter J (1969). "Heusler alloys". Contemporary Physics. 10 (6): 559–577. Bibcode:1969ConPh..10..559W. doi:10.1080/00107516908204800.
[edit]